High Temperature and Creep-resistant Filler Metals – SMAW Covered Electrodes EN ISO 3580-A:2008: EN ISO 3580-B:2008: AWS A5.5-06: AWS A5.5M-06:
E CrMo9 B 4 2 H5 E6218-9C1M H5 E8018-B8 E5518-B8
BÖHLER FOX CM 9 Kb SMAW basic electrode, high-alloyed, high temperature
Description Basic alloyed core wire electrode for high temperature steels and steels for hot hydrogen service, particularly in the petrochemical industry. Preferably used for 9% Cr 1% Mo steels e.g. X12CrMo9-1 (P9). Approved in long-term condition up to +600 °C service temperature. The weld metal is heat treatable. Metal recovery approx. 115 %. Detailed information on welding technology available on request.
Typical Composition of All-weld Metal Wt-%
C 0.08
Si 0.25
Mn 0.65
Cr 9.0
Mo 1.0
Mechanical Properties of All-weld Metal (*) a Yield strength Re N/mm2 (MPa): 610 (≥ 550) Tensile strength Rm N/mm2 (MPa): 730 (≥ 690) Elongation A (L0=5d0) %: 20 (≥ 319) Impact work ISO-V KV J + 20 °C: 70 (≥ 355) (*) a annealed, 760 °C/1 h/furnace down to 300 °C/air v quenched/tempered, 930 °C/10 min/air + 740 °C/2 h/air
v 600 730 25 100
(≥ (≥ (≥ (≥
550) 690) 319) 355)
Operating Data re-drying if necessary: ø mm L mm 300 - 350 °C, mind. 2 h 2.5 250 electrode identification: 3.2 350 FOX CM 9 Kb 8018-B8 E CrMo9 B 4.0 350 Preheating and interpass temperatures 250-350 °C. Post weld annealing least 1 hr followed by cooling in furnace down to 300 °C and still air.
Base Materials highly high temperature steels, same alloyed 1.7386 X12CrMo9-1, 1.7388 X7CrMo9-1, 1.7389 GX12CrMo10 ASTM A217 Gr. C12; A 234 Gr. WP9; A335 Gr. P9
Approvals and Certificates TÜV-D (2183.), TÜV-A (522), VUZ, SEPROZ, CE
Same Alloy Filler Metals GTAW rod: CM 9-IG
2-118
amps A 70 - 190 100 - 130 130 - 160 at 710-760°C for at
1. THE 2 dominant paradigms for brain-computer inter- facing today rely on noninvasive ... Departments of 1Computer Science and Engineering, 2Physiology and ... were found to overlap to a large degree in the recorded hemisphere. ... Patient 1. This 2
In the course of this experiment the early morning water potential (measured ..... waxes in Norway spruce by motor vehicle emissions. Eur J For Pathol 17, 444- ...
Policy Research Working Papers are available online at ... trade multiplier). .... programs and policies of the World Bank/IMF, other multi-lateral and bilateral ...